Thermostability,oxidation, and high-temperature tribological properties of nano-multilayered AlCrSiN/VN coatings

In this study, monolithic AlCrSiN, VN, and nano-multilayered AlCrSiN/VN coatings were deposited using a hybrid deposition system combining arc ion plating and pulsed direct current magnetron sputtering. The microstructure, thermostability, mechanical, oxidation and tribological properties of the coatings were comparably investigated. The multilayered AlCrSiN/VN coating exhibited a face-centered cubic (fcc) structure with (200) preferred orientation and showed the highest hardness (30.7 ± 0.5 GPa) among these three coatings due to the multilayer interface enhancement mechanism and higher compressive stress. The AlCrSiN sublayers effectively prevented the V element from rapid outward diffusion to the surface of AlCrSiN/VN coating at elevated temperatures, which improved the oxidation resistance of the coating. Decomposition of V (Cr)–N bonds occurred at annealing temperatures from 800 °C to 1000 °C and V₂N phase appeared at 1100 °C. The AlCrSiN/VN coating showed excellent tribological performance at high temperatures by combining the merits of VN layers for low friction coefficient and AlCrSiN layers for superior oxidation resistance. Compared to VN and AlCrSiN coatings, AlCrSiN/VN coating showed the lowest wear rate of 2.6×10^-15 m³/N·m at 600 °C and lowest friction coefficient of 0.26 at 800 °C with a relativity low wear rate of 39.4×10^-15 m³/N·m.