Crack-healing behaviour of MoSi2 dispersed Yb2Si2O7 environmental barrier coatings

MoSi₂ doped Yb₂Si₂O₇ composites were designed to extend the lifetime of Yb₂Si₂O₇ environmental barrier coatings (EBCs) via self-healing cracks during high-temperature applications. Yb₂Si₂O₇–Yb₂SiO₅–MoSi₂ composites with different mass fractions were prepared by applying spark plasma sintering. X-ray diffraction results confirmed that the composites consisted of Yb₂Si₂O₇, Yb₂SiO₅, and MoSi₂. The thermal expansion coefficients (CTEs) of the composites increased with an increase in the MoSi₂ content. The average CTE of the 15 wt% MoSi₂ doped Yb₂Si₂O₇ composite was 5.24 × 10^?6 K^?1, indicating that it still meets the CTE requirement of EBC materials. After being pre-cracked by using the Vickers indentation technique, the samples were annealed for 0.5 h at 1100 or 1300 °C to evaluate the crack-healing ability. Microstructural studies showed that cracks in 15 wt% MoSi₂ doped Yb₂Si₂O₇ composites were fully healed during annealing at 1300 °C. Two mechanisms may be responsible for crack healing. First, the cracks were filled with SiO₂ glass formed by MoSi₂ oxidation. Second, the formed SiO₂ continued to react with Yb₂SiO₅ to form Yb₂Si₂O₇, which can cause cracks to heal owing to volumetric expansion. The Yb₂Si₂O₇ formation with smaller volume expansion is more beneficial.