Effect of MgO/Al2O3 ratio on the crystallization behaviour of Li2O–MgO–Al2O3–SiO2 glass-ceramic and its wettability on Si3N4 ceramic

The composition governs the crystallization ability, the type and content of crystal phases of glass-ceramics. Glass-ceramic joining materials have generated more research interest in recent years. Here, we prepared a novel Li₂O–MgO–Al₂O₃–SiO₂ glass-ceramic for the application of joining Si₃N₄ ceramics. We investigated the influence of the MgO/Al₂O₃ composition ratio on microstructure and crystallization behaviour. The crystallization kinetics demonstrated that the glasses had excellent crystallization ability and high crystallinity. β-LiAlSi₂O₆ and Mg₂SiO₄ were precipitated from the glass-ceramics, and the increase of MgO concentration was conducive to the precipitation of Mg₂SiO₄. Among the glass-ceramic samples, the thermal expansion coefficient of LMAS2 glass-ceramic was 3.1 × 10^?6/°C, which was very close to that of Si₃N₄ ceramics. The wetting test showed that the final contact angle of the glass droplet on the Si₃N₄ ceramic surface was 32° and the interface was well bonded.