Magnetic field-enhanced photocatalytic nitrogen fixation over defect-rich ferroelectric Bi2WO6

Photocatalytic N₂ fixation is a promising and sustainable manufacturing process of ammonia (NH₃); however, the NH₃ production rate by this method is very low, thus severely restricting further application of this sustainable technology. Therefore, developing an efficient photocatalyst for N₂ fixation under mild conditions is urgently required. Herein, ferroelectric Bi₂WO₆ materials with different surface oxygen defects were prepared, and the concentration of corresponding defects was controlled by adjusting the thermal reduction time. The abundant oxygen defects in Bi₂WO₆ can provide more reactive sites to promote the effective adsorption of N₂, and the photogenerated charge carrier can be efficiently separated benefiting from the internal electric field. These would weaken the N₂ triple bond and reduce the activation energy barrier for the conversion of N₂ to NH₃ under mild conditions. In the absence of sacrificial agents and cocatalysts, the optimized Bi₂WO₆ with oxygen defects shows an indigenous NH₃ yield of 132.175 μmol·g^-1·L^-1·h^-1, which is more than two times higher than that of the original Bi₂WO₆. Surprisingly, the Bi₂WO₆ with oxygen defects produced more than eight times NH₃ (471.13 μmol·g^-1·L^-1·h^-1) than that of the original Bi₂WO₆ when assisted by an external magnetic field, thus providing a new perspective for further enhancing the N₂ fixation performance.