Preparation and characterization of Y3Al5O12 (YAG) nano-powder by co-precipitation method |
| |
| Authors: | J. Su Q.L. Zhang C.J. Gu D.L. Sun Z.B. Wang H.L. Qiu A.H. Wang S.T. Yin |
| |
| Affiliation: | Anhui Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, Hefei 230031, PR China |
| |
| Abstract: | YAG precursor was synthesized by a co-precipitation method from a mixed solution of aluminum and yttrium nitrates with aqueous ammonia as the precipitator. The structure, phase evolution and morphology of YAG precursor and the sintered powders were studied by means of IR, TG/DTA, XRD, TEM methods. It was found the precursor with approximate composition of Al(OH)3·0.3[Y2(OH)5·(NO3)2·2H2O] directly transformed to pure-YAG phase at 800 °C and no intermediate phases were detected. YAG nanocrystalline powders from sintering the precursor at different temperatures were less-aggregated and the diameters of the grains were about 40-100 nm. BET surface area of the particles decreased with increase of calcination temperature and the powder sintered at 800 °C can be used for fabrication of transparent YAG ceramics. |
| |
| Keywords: | A. Nanostructures B. Chemical synthesis |
| 本文献已被 ScienceDirect 等数据库收录！ |