Subsolidus phase equilibria and the Li5Nd4FeO10 phase in the Li2O-Nd2O3-Fe2O3 system |
| |
Authors: | I Ban M Drofenik D Suvorov |
| |
Affiliation: | a Faculty of Chemistry and Chemical Engineering, University of Maribor, Smetanova 17, 2000 Maribor, Slovenia b “Jozef Stefan” Institute, Jamova 39, 1000 Ljubljana, Slovenia |
| |
Abstract: | A survey of the subsolidus phase equilibria in the system Li2O-Nd2O3-Fe2O3 was made at subsolidus temperatures in the range 1000-1050 °C. A ternary phase was identified. The phase is centered on Li5Nd4FeO10, with a cubic lattice a = 11.9494 Å. The compound melts incongruently at 1105 °C. The magnetic susceptibility was measured in the temperature range 4-300 K. The compound is paramagnetic in the temperature range 150-300 K and follows the Curie-Weiss law. At about TN = 10 K, a long-range magnetic ordering is observed. |
| |
Keywords: | C Differential scanning calorimetry (DSC) C Thermogravimetric analysis (TGA) C X-ray diffraction D Magnetic properties D Phase equilibrium |