Synthesis and electrical properties of ordered perovskite oxide Cd3−x−yCuxAyTeO6 (A = Li, Na; 0.00 ≤ x, y ≤ 0.15)

Polycrystalline Cd_3−x−yCu_xA_yTeO₆ (A = Li, Na) samples were prepared by solid-state reaction, and their crystal structure and electrical properties were investigated. In Cd_3−xCu_xTeO₆ and Cd_3−yA_yTeO₆ (A = Li, Na), the maxim solubility of x and y was 0.15 and 0.15 for A = Li, 0.05 for A = Na, respectively. For co-substituted samples Cd_2.9−yCu_0.1Li_yTeO₆ and Cd_2.9−yCu_0.1Na_yTeO₆, the maxim solubility of x was the same as single substitution above-mentioned. The alkali-metal substituted samples Cd_3−yA_yTeO₆ (A = Li, Na) showed a negative Seebeck coefficient, which indicates that the major conduction carriers are electron. On the other hand, the co-substituted samples Cd_2.9−yCu_0.1A_yTeO₆ (A = Li, Na) represented a positive Seebeck coefficient, and major conduction carriers were hole through substitution by copper ions.