Microstructures of YBa2Cu3O7/La0.7Ca0.3MnO3 and La0.7Ca0.3MnO3/YBa2Cu3O7 bi-layers grown on (001)LaAlO3

Epitaxial YBa₂Cu₃O₇/La_0.7Ca_0.3MnO₃ (YBCO/LCMO) bi-layers and La_0.7Ca_0.3MnO₃/YBa₂Cu₃O₇ (LCMO/YBCO) bi-layers were grown on (001)LaAlO₃ by pulsed laser deposition, and their microstructures were compared by transmission electron microscopy investigation. In the YBCO(100 nm)/LCMO(150 nm) bi-layers, the LCMO layer consists of columnar grains of ~ 17 nm in diameter and contains mixed orientation domains of 100]_c, 010]_c and 001]_c. The YBCO layer is totally c-axis oriented and the YBCO lattices are tilted − 2.5° to + 2.5° as they grew on the rough surfaces of LCMO columnar grains. For the LCMO(140 nm)/YBCO(140 nm) bi-layers, the LCMO/YBCO interface is sharp and flat. The initial 12-nm thickness of the YBCO layer is composed of c-axis oriented domains, and the upper part of YBCO layer is 100] oriented. The LCMO layer was predominantly 001]_c oriented while 100]_c-oriented domains were occasionally observed.