Relationship between microstructure and tensile properties on a near-β titanium alloy after multidirectional forging and heat treatment |
| |
引用本文: | Zhi-Dan Lü,Chang-Jiang Zhang,Zhao-Xin Du,Jian-Chao Han,Shu-Zhi Zhang,Fei Yang,Yu-Yong Chen.Relationship between microstructure and tensile properties on a near-β titanium alloy after multidirectional forging and heat treatment[J].稀有金属(英文版),2019(4). |
| |
作者姓名: | Zhi-Dan Lü Chang-Jiang Zhang Zhao-Xin Du Jian-Chao Han Shu-Zhi Zhang Fei Yang Yu-Yong Chen |
| |
摘 要: | In this study, a new near-beta titanium alloy, Ti-4Al-1Sn-2Zr-5Mo-8V-2.5Cr, was prepared by induction skull melting(ISM) and multidirectional forging. The effect of aging heat treatment on microstructure and tensile properties of the alloy after solution treatment in the twophase(α + β) region was investigated. The micros tructure results show that the globular primary α phase(α_p) and the needle-like secondary α phase(α_s) are precipitated in the β matrix. The size of α_s increases with the increase in aging temperature,while the content of α_s goes up to a peak value and then decreases. The tensile testing results show that the strength increases first and then decreases with the increase in temperature. The variation of ductility presents the opposite way compared with the trend of strength level.When aged at 500 ℃, the alloy exhibits an excellent balance of tensile strength(1529 MPa) and elongation(9.22%). And the relative mechanism of strengthening and toughening was analyzed and discussed.
|
本文献已被 CNKI 等数据库收录! |
|