Effect of Ti layer thickness on microstructure and magnetic properties of Ti/Co/Ti films
Authors:ZHANG Yujie  ZHANG Hanwei  FENG Shunzhen  SUN Huiyuan  HU Yanying  PENG Yan
Abstract:TiCoTi granular films were prepared by DC facing-target magnetron sputtering system onto glass substrates and subsequently in situ annealing in vacuum. Structural of Ti ( t nm)/Co (40 nm)/Ti ( t nm) films were investigated in detail, which shows that the majority Co nanograins are formed as the hexagonal-close-packed (HCP) structure. Vibrating sample magnetometer (VSM) and scanning probe microscope (SPM) were applied to study the magnetic properties, morphologies and domain structures of these samples. It has been found that the structure and magnetic properties of the Ti/Co/Ti films depend strongly on the Ti layer thickness. The out-of-plane coercivities ( Hc) of the film is maximum about 78.8 kA·m-1 when t =5 nm with annealing at 300 ℃; the distributing of grains of the sample is uniformity; and the average size of particles is about 13 nm. The obtained results suggest that this system is perpendicular anisotropy and might be applicable to perpendicular magnetic recording media.
Keywords:facing-target magnetron sputtering  perpendicular magnetic recording  HCP-structure  coercivity
本文献已被 万方数据 等数据库收录!
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号