Phase relationship on Mo-S system at high temperatures

Changing the partial pressure of sulfur Ps₂ at temperatures of 750° and 950°C, phase equilibria on the Mo-S system by solid-gas reaction were investigated. Hexagonal 2H-MoS₂ and monoclinic Mo₂S₃ phases were identified from the x-ray powder diffraction pattern. The 2H-MoS₂ had a slight homogeneity range, i.e. MoS_1.978 to MoS_2.0 at 950°C, MoS_1.983 to MoS_2.0 at 750°C. No remarkable variation of lattice parameters for the MoS₂ was observed. The composition of the Mo₂S₃ phase was not stoichiometric MoS_1.5 but MoS_1.457 at 950°C. At 750°C the composition of the Mo₂S₃ phase could not be determined since it was quite difficult to establish the equilibrium state between the gas and the condensed phases. This finding agreed well with the result of Morimoto and Kullerud.