Structural characterization and properties enhancement of diamond-like carbon films synthesized under low energy Ne bombardment

Diamond-like carbon (DLC) films were synthesized by Ar⁺ sputtering graphite with concurrent Ne⁺ bombardment. Transmission electron microscopy diffraction revealed that some diamond crystals were distributed in the amorphous matrix of DLC films synthesized under Ne⁺ bombardment at an energy of 200 eV and ion current density of 0.19 mA cm⁻². X-ray photo electron spectra showed that the valence band of the DLC films was similar to that of diamond, and the binding energy of electrons was 284.9 eV. The DLC films possessed a high hardness of 42.14 GPa and excellent wear resistance. It was confirmed that the wide atomic intermixed film-substrate interface meant that the DLC films would improve greatly the wear-resistant properties of AISI 52100 steel if the DLC films were coated on its surface.