Preparation and Characterization of Super Absorbent Resin from Natural Cellulose

The grafting polyacrylamide onto wood pulp cellulose (cell-g-PAM) was performed with cerous ammo-nium nitrate as the initiator and hydrolyzed to produce the super absorbent resin. The FTIR shows that the poly-acrylamide is grafted on the cellulose. After hydrolyzation, part of acrylamino groups are transformed into car-boxyl groups. The XRD analysis shows that the graft polymerization occurred at the amorphous section and the surface of the crystal section of cellulose. The SEM graph reveals that there is a layer of polymer on the surface of cellulose fiber and the fibril structure of the cellulose surface is covered. After hydrolyzation, the surface of the product is different from that of cell-g-PAM‘s and the surface is scraggy. The technical conditions to prepare high water absorbent resin were confirmed. Through the radical graft copolymerization, the high water absorbent resin can be produced from wood pulp cellulose.

Preparation and Characterization of Super Absorbent Resin from Natural Cellulose

The grafting polyacrylamide onto wood pulp cellulose (cell g PAM) was performed with cerous ammonium nitrate as the initiator and hydrolyzed to produce the super absorbent resin. The FTIR shows that the polyacrylamide is grafted on the cellulose. After hydrolyzation, part of acrylamino groups are transformed into carboxyl groups. The XRD analysis shows that the graft polymerization occurred at the amorphous section and the surface of the crystal section of cellulose. The SEM graph reveals that there is a layer of polymer on the surface of cellulose fiber and the fibril structure of the cellulose surface is covered. After hydrolyzation, the surface of the product is different from that of cell g PAM's and the surface is scraggy. The technical conditions to prepare high water absorbent resin were confirmed. Through the radical graft copolymerization, the high water absorbent resin can be produced from wood pulp cellulose.