| 摘 要： | 采用熔盐法在K2CO3和Na2CO3的熔盐（K2CO3／Na2CO3=45／55）中800℃并保温2h的条件下制备出了单相、纯钙态矿型结构的Na0.5K0.5NbO3粉体，运用XRD以及SEM技术对所得粉体进行了相组成及显微结构分析。结果表明：随着盐含量的增加，晶体结构从正交相转变为四方相，晶粒大小先增加而后稍微减小，并且获得较好的介电压电性：ε33^T／ε0（1kHz）=45-264，tgδ=1．5％～2．6％，Tc=402℃，Tτ-o=202℃，d33=88-98pC／N，Qm=465-574，Kp=29．09%～30．47％，在10kHz频率下，介电损耗有一点改变。NKN将有可能成为用于高频下的无铅压电陶瓷之一。
|
| 关 键 词： | 无铅压电陶瓷 熔盐法 XRD 介电压电性 |
| 文章编号： | 1001-9731(2005)12-1974-03 |
| 收稿时间： | 2005-02-25 |
| 修稿时间： | 2005-06-04 |
The preparation of (Na0.5K0.5) NbO3 powder by molten salt synthesis |
| |
| FAN Ya-hong,SUN Qing-chi,WANG Yu-bin,PAN Tie-zheng,LU Cui-min. The preparation of (Na0.5K0.5) NbO3 powder by molten salt synthesis[J]. Journal of Functional Materials, 2005, 36(12): 1974-1976 |
| |
| Authors: | FAN Ya-hong SUN Qing-chi WANG Yu-bin PAN Tie-zheng LU Cui-min |
| |
| Affiliation: | Department of Materials Engineering, Tianjin University, Tianjin 300072, China |
| |
| Abstract: | The (Na0.5K0.5)NbO3 powder with single-phase, pure perovskite was prepared at 800℃ for 2h in molten salt (K2CO3/Na2CO3 =45/55),which was characterized by the X-ray diffraction and SEM technique. It was found that the crystal structure changes from orthorhombic phase to tetragonal phase and grain size increases and then reduces a little with the increasing of salt.Good dielectric and piezoelectric properties can be observed: εT33/ε0 (1kHz) = 45 ～ 264, tgδ= 1.5 % ～ 2.6%, Tc = 402 ℃, TT-o =202℃ ,d33 =88～98pC/N, Qm =465～574, Kp =29.09%～30.47% and in the frequency of 10kHz, the dielectric loss changed a little. |
| |
| Keywords: | lead free piezoelectric ceramics molten salt synthesis X-ray diffraction dielectric and piezoelectric properties |