Heat‐Transport Mechanisms in Superlattices

The heat transport mechanisms in superlattices are identified from the cross‐plane thermal conductivity Λ of (AlN)_x–(GaN)_y superlattices measured by time‐domain thermoreflectance. For (AlN)_{4.1 nm}–(GaN)_{55 nm} superlattices grown under different conditions, Λ varies by a factor of two; this is attributed to differences in the roughness of the AlN/GaN interfaces. Under the growth condition that gives the lowest Λ, Λ of (AlN)_{4 nm}–(GaN)_y superlattices decreases monotonically as y decreases, Λ = 6.35 W m⁻¹ K⁻¹ at y = 2.2 nm, 35 times smaller than Λ of bulk GaN. For long‐period superlattices (y > 40 nm), the mean thermal conductance G of AlN/GaN interfaces is independent of y, G ≈ 620 MW m⁻² K⁻¹. For y < 40 nm, the apparent value of G increases with decreasing y, reaching G ≈ 2 GW m⁻² K⁻¹ at y < 3 nm. MeV ion bombardment is used to help determine which phonons are responsible for heat transport in short period superlattices. The thermal conductivity of an (AlN)_{4.1 nm}–(GaN)_{4.9 nm} superlattice irradiated by 2.3 MeV Ar ions to a dose of 2 × 10¹⁴ ions cm⁻² is reduced by <35%, suggesting that heat transport in these short‐period superlattices is dominated by long‐wavelength acoustic phonons. Calculations using a Debye‐Callaway model and the assumption of a boundary scattering rate that varies with phonon‐wavelength successfully capture the temperature, period, and ion‐dose dependence of Λ.