Use of glass waste as an activator in the preparation of alkali-activated slag. Mechanical strength and paste characterisation |
| |
| Affiliation: | 1. Department of Civil Engineering, Chung Yuan Christian University, Chung Li 32023, Taiwan, ROC;2. Department of Civil Engineering, National Kaohsiung University of Applied Sciences, 807, Taiwan, ROC;1. Delft University of Technology, Department of Chemical Engineering, Product and Process Engineering Group, Julianalaan 136, 2628 BL Delft, The Netherlands;2. Delft University of Technology, Department of Biotechnology, Environmental Biotechnology Group, Julianalaan 67, 2628 BC Delft, The Netherlands;1. Laboratory of Applied Inorganic Chemistry, University of Yaounde I, Faculty of Science, Department of Inorganic Chemistry, PO Box 812, Yaounde, Cameroon;2. Institut für Mineralogie, Leibniz Universität Hannover, Callinstrasse 3, D-30167 Hannover, Germany;3. Local Materials Promotion Authority, PO Box: 2396, Nkolbikok, Yaoundé, Cameroon;4. Department of Engineering Enzo Ferrari, University of Modena and Reggio Emilia, Via Vivarelli 10, Modena, Italy |
| |
| Abstract: | The alkaline activation of aluminosilicates yields alkaline cements, eco-efficient alternatives to ordinary Portland cements. Alkaline cements and concretes exhibit highest strength and longest durability when activated with a solution of alkaline silicate hydrates (waterglass). To obtain these alkaline silicates, however, an aqueous solution of the proper proportion of carbonate and silica salts must be heated to temperatures of around 1300 °C. The present paper explores the feasibility of using urban and industrial glass waste as a potential alkaline activator for blast furnace slag (AAS).AAS pastes were prepared with three activators: waterglass, a NaOH/Na2CO3 mix and the solutions resulting from dissolving glass waste in NaOH/Na2CO3. Mechanical, mineralogical (XRD, FTIR) and microstructural (porosimetry, NMR and SEM/EDX) trials were conducted to characterise the pastes obtained.The findings proved the feasibility of using glass waste to alkali activate slag. Treating glass waste with NaOH/Na2CO3 (pH = 13.6) favours the partial dissolution of the Si in the glass into its most reactive monomeric form.The solutions resulting from the treatment of glass waste act as alkaline activators, partially dissolving vitreous blast furnace slag. The composition and microstructure of the reaction products identified in the two types of paste were similar. Strength and microstructural development in the pastes activated with glass waste were also comparable to the parameters observed in AAS pastes prepared with conventional activators. |
| |
| Keywords: | |
| 本文献已被 ScienceDirect 等数据库收录！ |
|