The corrosion of two NiNb alloys under 1 atm O2 at 600–800 °C

The oxidation of two NiNb alloys containing 15 and 30 wt% Nb has been studied at 600–800 °C in pure oxygen under 1 atm O₂ at 600–800 °C. The scales formed on both alloys under all conditions show an external scale, generally duplex, containing an outermost layer of nearly pure NiO and an innermost region of NiO mixed with the double NiNb oxide NiNb₂O₆. Moreover, the samples corroded at all temperatures also show a region of internal oxidation composed of a mixture of alpha nickel and niobium oxides (Nb₂O₅ or/and NbO₂), which formed from both alloy phases Ni₈Nb and Ni₃Nb. No important depletion of niobium was observed in the alloy close to the interface with the zone of internal oxidation, while the depth of this region is generally much higher than measured for the corrosion of the same alloys under low oxygen pressures at the same temperatures. The corrosion mechanism of these alloys is examined with special reference to the effects of the low solubility of niobium in nickel.