| Abstract: | Resol was solution‐blended with vinyl acetate‐2‐ethylhexyl acrylate (VAc–EHA) resin in an aqueous medium, in varying weight fractions, with hexamethoxymethylmelamine (HMMM) as a crosslinker and the data were compared with a control. The present work was aimed to obtain an optimum combination of high‐temperature resistance by synthesis of an interpenetrating network (IPN) of the resins. The control gave a semi‐IPN system, in which the resol crosslinked, while the acrylic did not, whereas the blend, where HMMM was the crosslinker, gave a full‐IPN system. FTIR spectra of the blends of resol/VAc–EHA/HMMM indicated the formation of new stretching, which was generated due to crosslinking reactions among VAc–EHA and the crosslinker HMMM. TGA showed that, with an increase in the VAc–EHA percent in semi‐IPNs, the decomposition temperature decreased gradually, whereas in case of full‐IPNs, the decomposition temperature increased with increase in the VAc–EHA percent. However, the full‐IPNs had a higher decomposition temperature than that of the semi‐IPNs, at the same resol/(VAc–EHA) ratio. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 86: 3581–3588, 2002 |