Synergistic effect of TiO2 and iron oxide supported on fluorocarbon films. Part 1: Effect of preparation parameters on photocatalytic degradation of organic pollutant at neutral pH

Iron oxide and TiO₂ were immobilized on modified polyvinyl fluoride films in a sequential process. Synergic effects of iron oxide and TiO₂ on the polymer film were observed during the heterogeneous degradation of hydroquinone (HQ) in the presence of H₂O₂ at pH close to neutrality and under simulated solar irradiation. Within the degradation period, little iron leaching (<0.5 mg/L) was observed.The surface of commercial polyvinyl fluoride (PVF) film was modified by TiO₂ under light inducing oxygen group (C–OH, CO, COOH) formation on the film surface. During this treatment, TiO₂ nanoparticles simultaneously bind to the film, leading to PVF^f–TiO₂. The possible mechanistic pathway for the TiO₂ deposition and the nature of the polymer–TiO₂ interaction are discussed. Furthermore PVF and PVF^f–TiO₂ were immersed in an aqueous solution for the deposition of iron oxide layer by hydrolysis of FeCl₃, leading to PVF–Fe oxide and to PVF^f–TiO₂–Fe oxide respectively.HQ degradation and mineralization mediated by PVF^f–TiO₂, PVF–Fe oxide and PVF^f–TiO₂–Fe oxide were investigated under different conditions. Remarkable synergistic effects were observed for PVF^f–TiO₂–Fe oxide possibly due to Fe(II) regeneration, accelerated by electron transfer from TiO₂ to the iron oxide under light.