Stress Corrosion Cracking of X80 Pipeline Steel in Near-Neutral pH Environment under Constant Load Tests with and without Preload |
| |
| Authors: | YZ Jia JQ Wang EH Han and W Ke State |
| |
| Affiliation: | Key Laboratory for Corrosion and Protection, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China 2) Department of Electromechanical Engineering, Sichuan College of Architectural Technology, Deyang 318000, China |
| |
| Abstract: | Constant load tests in NS4 solution purged with N2–5%CO2 gas mixture were conducted on American Petroleum Institute (API) X80 pipeline steel applied in the 2nd West-East Gas Pipeline project with and without preload. The results show that cracks could initiate and propagate in X80 pipeline steel in near-neutral pH environment under a constant load condition. The life of crack initiation and propagation increased with decreasing applied stress. Preload did not change its corrosion behavior obviously. However, preload reduced the time for crack initiation. |
| |
| Keywords: | Stress corrosion cracking X80 pipeline steel Near-neutral pH solution Preload |
| 本文献已被 CNKI 等数据库收录！ |
|