| Ti/La_(0.7)Ca_(0.3)MnO_3/Pt结构器件中“负”电阻开关特性研究 |
| |
| 引用本文： | 刘新军,李效民,王群,杨蕊,曹逊,陈立东.Ti/La_(0.7)Ca_(0.3)MnO_3/Pt结构器件中“负”电阻开关特性研究[J].无机材料学报,2010,15(2):151-156. |
| |
| 作者姓名： | 刘新军 李效民 王群 杨蕊 曹逊 陈立东 |
| |
| 作者单位： | (1.中国科学院上海硅酸盐研究所高性能陶瓷和超微结构国家重点实验室,上海200050;2.中国科学院研究生院,北京100049); |
| |
| 基金项目： | 国家自然科学基金(50672116); 国家高技术研究发展计划863项目(2006AA03Z308) |
| |
| 摘 要： | 以Pt/Ti/SiO2/Si为衬底,制备了具有电阻转变特性的Ti/La0.7Ca0.3MnO3(LCMO)/Pt结构器件.X射线衍射分析表明LCMO薄膜呈纳米晶或非晶态,扫描电子显微镜及原子力显微镜分析表明LCMO薄膜表面平整、光滑致密.电学测试结果表明Ti/LCMO/Pt结构具有明显的双极型"负"电阻转变特性,低电阻态的导电过程为空间电荷限制电流机制,高电阻态的导电过程为Poole-Frenkel发射机制.利用氧化还原反应的随机性和TiOx中间层空间分布的不均匀性,定性地解释了高电阻态的不稳定性以及电流-电压曲线上的电流突变现象.
|
| 关 键 词： | 脉冲激光沉积法 电阻开关 电脉冲诱发电阻转变 锰氧化物薄膜 |
| 收稿时间： | 2009-6-22 |
| 修稿时间： | 2009-8-27 |
Study on the Negative Resistance Switching Properties in Ti/La_(0.7)Ca_(0.3)MnO_3/Pt Sandwiches Devices |
| |
| LIU Xin-Jun,LI Xiao-Min,WANG Qun,YANG Rui,CAO Xun,CHEN Li-Dong.Study on the Negative Resistance Switching Properties in Ti/La_(0.7)Ca_(0.3)MnO_3/Pt Sandwiches Devices[J].Journal of Inorganic Materials,2010,15(2):151-156. |
| |
| Authors: | LIU Xin-Jun LI Xiao-Min WANG Qun YANG Rui CAO Xun CHEN Li-Dong |
| |
| Affiliation: | (1.StateKeyLaboratoryofHighPerformanceCeramicsandSuperfineMicrostructures,ShanghaiInstituteofCeramics,ChineseAcademyofSciences,Shanghai200050,China;2.GraduateUniversityoftheChineseAcademyofScience,Beijing100049,China) |
| |
| Abstract: | The La0.7Ca0.3MnO3(LCMO) thin films with resistive switching properties were grown on Pt(111)/Ti/SiO2/Si substrates by pulsed laser deposition(PLD).X-ray diffraction(XRD) results show that the films exhibited nanocrystalline or noncrystalline.Scanning electrical microscope(SEM) and atomic force microscope(AFM) were employed to characterize the morphology of as-grown films whose surfaces are flat,smooth and dense.The results of electrical test indicate that the Ti/LCMO/Pt structures show a bipolar 'negative'... |
| |
| Keywords: | pulsed laser deposition(PLD) resistive switching behaviors electric-pulse-induced resistance switching manganite films |