通过大气暴露试验和实验室的浸渍干燥湿润复合循环试验，结合腐蚀产物的表面分析，研究了4种钢在沈阳地区的大气腐蚀规律和模拟大气腐蚀过程的腐蚀规律.结果表明：在大气暴露试验和室内模拟加速腐蚀试验中，4种钢的腐蚀产物都具有不同程度的保护性，腐蚀规律可用ΔW=Ktn公式描述，室内外腐蚀试验结果有较好的相关性.采用001 mol/L NaHSO3+0.001 mol/L NaCl介质为加速剂, 通过干湿复合 循环试验,可模拟钢在沈阳大气环境中的腐蚀过程，近似推测户外长期暴露试验的结果.

INVESTIGATION ON INTERRELATION OF INDOOR ACCELERATED CORROSION AND ATMOSPHERIC EXPOSURE CORROSION OF STEELS

The law of atmospheric corrosion of 4 steels in Shenyang area was studied by means of atmospheric exposure tests and their corrosi on products were analyzed by XRD and IRAS.For comparison,an accelerated weathering tests of immersion-dry-wet combined cycles with the medium of NaHSO3 and NaCl was used to simulate the field corrosion process.The results showed that,in the two conditions of field and laboratory,the corrosion process of steels could be described by a formulary of ΔW =Ktn;the main corrosion products are α-FeOOH and γ-FeOOH.It is obvious that there exists a rather good the interrelation between simulating accelerated corrosion and atmos-pheric exposure corrosion.The corrosion process of steels in Shenyang atmosphere could be simulated by accelerated weathering tests of immersion-dry-wet combined cycles with the medium of 0.01 mol/L NaHSO3 and 0.001 mol/L NaCl. 