Regeneration of NOx trap catalysts

We have investigated the regeneration of a nitrated or sulphated model Pt/Ba-based NO_x trap catalyst using different reductants. H₂ was found to be more effective at regenerating the NO_x storage activity especially at lower temperature, but more importantly over the entire temperature window after catalyst ageing. When the model NO_x storage catalyst is sulphated in SO₂ under lean conditions at 650 °C almost complete deactivation can be seen. Complete regeneration was not achieved, even under rich conditions at 800 °C in 10% H₂/He. Barium sulphate formed after the high temperature ageing was partly converted to barium sulphide on reduction. However, if the H₂ reduced sample was exposed to a rich condition in a gas mixture containing CO₂ at 650 °C, the storage activity can be recovered. Under these rich conditions the S^2? species becomes less stable than the CO₃^2?, which is active for storing NO_x. Samples which were lean aged in air containing 60 ppm SO₂ at <600 °C, after regeneration at λ=0.95 at 650 °C, have a similar activity window to a fresh catalyst. It is, therefore, important that CO₂ is present during the rich regenerations of the sulphated model samples (as of course it would be under real conditions), as suppression of carbonate formation can lead to sulphide formation which is inactive for NO_x storage.