Potential use of only Yb2O3 in producing dense Si3N4 ceramics with high thermal conductivity by gas pressure sintering

Yb₂O₃ is an efficient sintering additive for enhancing not only thermal conductivity but also the high-temperature mechanical properties of Si₃N₄ ceramics. Here we report the fabrication of dense Si₃N₄ ceramics with high thermal conductivity by the gas pressure sintering of α-Si₃N₄ powder compacts, using only Yb₂O₃ as an additive, at 1900 °C under a nitrogen pressure of 1 MPa. The effects of Yb₂O₃ content, sample packing condition and sintering time on the densification, microstructure and thermal conductivity were investigated. Curves of the density plotted against the Yb₂O₃ content exhibited a characteristic ‘N’ shape with a local minimum at 3 mol% Yb₂O₃ and nearly complete densification below and above this concentration. The effects of the sample packing condition on the densification, microstructure and thermal conductivity strongly depended on the Yb₂O₃ content. The embedded condition led to more complete densification but also to a decrease in thermal conductivity from 119 to 94 W m^-1 K⁻¹ upon 1 mol% Yb₂O₃ addition. The sample packing condition had little effect on the density and thermal conductivity (102–106 W m⁻¹ K⁻¹) at 7 mol% Yb₂O₃. The thermal conductivity value was strongly related to the microstructure.