Superplasticity in a thermomechanically processed High-Mg,Al-Mg alloy

Superplastic elongations in excess of 400 pct have been observed in tension testing at 573 K (300 °C) and strain rate έ= 2 × 10^-3 s^-1 for a thermomechanically processed Al-10.2 pct Mg-0.52 pct Mn alloy. The thermomechanical processing consists of solution treatment and hot working, followed by extensive warm rolling at 573 K (300 °C), a temperature below the solvus for Mg in the alloy. This processing results in a fine subgrain structure in conjunction with refined and homogeneously distributed β(Al₈Mg₅) and MnAl₆ precipitates. This structure does not statically recrystallize when annealed at 573 K (300 °C) but appears to recrystallize continuously during deformation at such a temperature and the resulting fine grain structure deforms with minimal cavitation. At temperatures above the Mg-solvus,e.g., 673 K (400 °C), recrystallization and growth occur readily resulting in rela tively coarser structures which deform superplastically but with extensive grain boundary sliding and cavitation. Formerly in Materials Group, Mechanical Engineering, Naval Postgraduate School Formerly Graduate Student in Mechanical Engineering, Naval Postgraduate School