Preparation of mullite monoliths with well-defined macropores and mesostructured skeletons via the sol–gel process accompanied by phase separation

Mullite monoliths with well-defined macropores and mesostructured skeletons have been prepared via the sol–gel process accompanied by phase separation in the presence of poly(ethylene oxide) (PEO). Gelation of Al₂O₃–SiO₂ binary system with chloride salts as an additional precursor has been mediated by propylene oxide (PO) as an acid scavenger, while PEO worked as a phase-separation inducer. The dried gel and that heat-treated at 800 °C are amorphous, and γ-Al₂O₃ or Si–Al spinel phase nanocrystals are crystallized at 900–1000 °C. After heat-treated at and above 1100 °C for 5 h, the complete crystalline mullite is generated, and the macroporous monoliths in large dimensions of more than 15 mm × 15 mm × 10 mm are obtained. Heat-treatment at 200–1400 °C does not basically spoil the macroporous structure of monoliths, while decreases the macropore size and significantly alters the phase compositions and micro-mesoporous structure.