| 铜合金铸锭典型缺陷产生的原因及解决办法 |
| |
| 引用本文： | 袁孚胜,郭峰. 铜合金铸锭典型缺陷产生的原因及解决办法[J]. 有色冶金设计与研究, 2014, 0(3): 27-28 |
| |
| 作者姓名： | 袁孚胜 郭峰 |
| |
| 作者单位： | 中国瑞林工程技术有限公司,江西南昌330031 |
| |
| 摘 要： | 总结了铜及其合金铸锭生产中产生的偏析、气孔、缩孔与缩松、夹杂、裂纹及冷隔等几种典型缺陷,并分析了这些缺陷产生的原因,探讨了相应的解决方法。
|
| 关 键 词： | 铜合金 铸锭 缺陷 原因分析 解决办法 |
Reason of Common Defect of Copper Alloy Ingot and Its Solution |
| |
| YUAN Fu-sheng,GUO Feng. Reason of Common Defect of Copper Alloy Ingot and Its Solution[J]. , 2014, 0(3): 27-28 |
| |
| Authors: | YUAN Fu-sheng GUO Feng |
| |
| Affiliation: | (China Nerin Engineering Co., Ltd., Nanchang, Jiangxi 330031, China) |
| |
| Abstract: | This paper summarizes such common defects as segregation, air hole, shrinkage hole and shrinkage porosity, inclusion, crack and cold shut produced during copper and its alloy ingot production, analyzes the caused reason and discusses corresponding solution. |
| |
| Keywords: | copper alloy ingot defect reason analysis solution |