Preparation by a Sol-Gel Process of Borosilicate Glasses Containing Microcrystals of Tellurium and Zinc Telluride

Borosilicate glasses, 5B₂O₃· 95SiO₂ (mol%), containing TeO₂ and ZnO nominally equivalent to 10 wt% Te and ZnTe were prepared by a solgel method from Si(OC₂H₅)₄, B(OCH₃)₃, H₆TeO₆, and Zn(NO₃)₂. A study by electron spectroscopy for chemical analysis (ESCA) showed that glasses heated at high temperature (450°C) in air contained both Te⁶⁺ and Te⁴⁺ ions on the surface layer, but that mainly Te⁴⁺ ions occurred inside the bulk glass. When solgel-derived borosilicate glasses containing the TeO₂ compound were reduced at elevated temperature in a hydrogen atmosphere, Te crystallites ranging in size from 4 to 15 nm were produced at a lower temperature, between 200° and 250°C. The absorption edge moved from the infrared to the visible wavelength region as the particle size decreased to about 4 nm. For glasses containing both TeO₂ and ZnO, ZnTe crystallites formed at high temperature—over 300°C—and existed along with the Te phase.