An electron microscopic and diffraction study of Cu-9 wt pct Al alloy

An electron microscopic investigation of Cu-9 wt pct Al alloy low thermal treated at 250°C for 30 min was performed in the deformed and non-deformed condition. For this composition and ordering treatment the alloy exhibits the higher increase in strength. It was found that the images formed in the non-deformed alloy, reveal the presence of ordered domains of an average size of 80?, being the amount of order dependent of whether or not quenched-in vacancies are present. It is probable that the domains nucleate preferentially at stacking faults in the deformed condition. A periodic antiphase structure was determined from computations and comparison with electron diffraction data. The superlattice cell is based on the LI₂ type, tetragonal face centered with a period approximately three times the lattice parameter of the matrix, having three variants of orientation within an ordered region.