Enhanced hydrogen storage performance of LiAlH4-MgH2-TiF3 composite

The mutual destabilization of LiAlH₄ and MgH₂ in the reactive hydride composite LiAlH₄-MgH₂ is attributed to the formation of intermediate compounds, including Li-Mg and Mg-Al alloys, upon dehydrogenation. TiF₃ was doped into the composite for promoting this interaction and thus enhancing the hydrogen sorption properties. Experimental analysis on the LiAlH₄-MgH₂-TiF₃ composite was performed via temperature-programmed desorption (TPD), differential scanning calorimetry (DSC), isothermal sorption, pressure-composition isotherms (PCI), and powder X-ray diffraction (XRD). For LiAlH₄-MgH₂-TiF₃ composite (mole ratio 1:1:0.05), the dehydrogenation temperature range starts from about 60 °C, which is 100 °C lower than for LiAlH₄-MgH₂. At 300 °C, the LiAlH₄-MgH₂-TiF₃ composite can desorb 2.48 wt% hydrogen in 10 min during its second stage dehydrogenation, corresponding to the decomposition of MgH₂. In contrast, 20 min was required for the LiAlH₄-MgH₂ sample to release so much hydrogen capacity under the same conditions. The hydrogen absorption properties of the LiAlH₄-MgH₂-TiF₃ composite were also improved significantly as compared to the LiAlH₄-MgH₂ composite. A hydrogen absorption capacity of 2.68 wt% under 300 °C and 20 atm H₂ pressure was reached after 5 min in the LiAlH₄-MgH₂-TiF₃ composite, which is larger than that of LiAlH₄-MgH₂ (1.75 wt%). XRD results show that the MgH₂ and LiH were reformed after rehydrogenation.