| 摘 要： | 本文研究了采用高温固相法合成的Ba3Gd(PO4)3:Dy3 荧光粉的阴极射线发光特性.测试并比较了电子轰击前后荧光粉的CL谱、色坐标以及PL谱变化.Ba3Gd(PO4)3:0.06Dy3 荧光粉的色坐标为 x=0.454,y=0.424,Tc=2889.3 K.测试结果显示该荧光粉是一种低色温、暖白光荧光粉,并且具有高的饱和电流,有耐大电流密度电子束轰击的能力.
|
| 关 键 词： | 阴极射线发光 荧光粉 Ba3GdPO43 Dy3 cathodoluminescence phosphor Ba3Gd(PO4)3:Dy3 荧光粉 阴极射线发光 研究 Properties high saturation currents bombardment results show color temperature chromaticity measurement International colour photoluminescence spectra Commission Cathodoluminescence synthesized |
| 文章编号： | 1005-9490（2008）01-0184-05 |
| 收稿时间： | 2007-04-30 |
| 修稿时间： | 2007年4月30日 |
Cathodoluminescent Properties of Ba3Ga(PO4)3 Dy'3+ Phosphor |
| |
| DUAN C Y,CHEN Jun,DENG S Z,XU N S,HAN Bing,LIANG H B,SU Qiang.Cathodoluminescent Properties of Ba3Ga(PO4)3 Dy'3+ Phosphor[J].Journal of Electron Devices,2008,31(1):184-188. |
| |
| Authors: | DUAN C Y CHEN Jun DENG S Z XU N S HAN Bing LIANG H B SU Qiang |
| |
| Affiliation: | State Key Laboratory of Optoelectronic Materials and Technologies |
| |
| Abstract: | Cathodoluminescent properties of Ba3Gd(PO4)3:Dy3+ phosphor were studied. The phosphor was synthesized by high-temperature solid-phase reaction. Cathodoluminescence spectra, the Commission In-ternational de l'Eclairage colour coordinates and photoluminescence spectra were determined. The Catho-doluminescence measurement shows that the Commission International de 1' Eclairage (CIE) chromaticity coordinates of Ba3Gd(PO4)3:0.06Dy3+ phosphor are x=0.454 and y=0.424, and the color temperature is 2889.3 K. The results show that the phosphor is a low color temperature, warm-white phosphor with high saturation currents and can endure high-current-density bombardment. |
| |
| Keywords: | cathodoluminescence phosphor Ba3Gd(PO4)3Dy3 |