Effect of the surface microstructure of SiC inner coating on the bonding strength and ablation resistance of ZrB2-SiC coating for C/C composites |
| |
Affiliation: | 1. C/C Composites Technology Research Center, Northwestern Polytechnical University, Xi''an, Shaanxi 710072 PR China;2. School of Mechanics, Civil Engineering & Architecture, Northwestern Polytechnical University, Xi''an, Shaanxi 710072 PR China |
| |
Abstract: | The present study has been conducted in order to investigate the effect of the surface morphology of SiC inner coating on the bonding strength and ablation resistance of the sprayed ZrB2-SiC coating for C/C composites. The microstructure of SiC inner coatings prepared by chemical vapor deposition and pack cementation at different temperatures were analyzed by X-ray diffraction, scanning electron microscopy, and 3D Confocal Laser Scanning Microscope. Tensile bonding strength and oxyacetylene ablation testing were used to characterize the bonding strength and ablation resistance of the sprayed ZrB2-SiC coating, respectively. Results show that SiC inner coating prepared by chemical vapor deposition has a smooth surface, which is not beneficial to improve the bonding strength and ablation resistance of the sprayed ZrB2-SiC coating. SiC inner coating prepared by pack cementation at 2000 °C has a rugged surface with the roughness of 72.15 µm, and the sprayed ZrB2-SiC coating with it as inner layer exhibits good bonding strength and ablation resistance. |
| |
Keywords: | Surface morphology Bonding strength Ablation resistance |
本文献已被 ScienceDirect 等数据库收录! |
|