Energy storage and release properties of Sr-doped (Pb,La)(Zr,Sn,Ti)O3 antiferroelectric ceramics |
| |
Affiliation: | 1. Electronic Materials Research Laboratory, Key Laboratory of the Ministry of Education, Xi''an Jiaotong University, Xi''an, Shaanxi 710049, People''s Republic of China;2. State Key Laboratory of Electrical Insulation and Power Equipment, Xi''an Jiaotong University, Xi''an, Shaanxi 710049, People''s Republic of China;1. State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing 100029, China;2. Beijing Key Laboratory of Fine Ceramics, State Key Laboratory of New Ceramics and Fine Processing, Institute of Nuclear and New Energy Technology, Tsinghua University, Beijing 100084 China;3. Ferroelectric Laboratory, Institute of Natural Science, Ural Federal University, Ekaterinburg 620000, Russia;1. Electronic Materials Research Laboratory, Key Laboratory of the Ministry of Education, Xi’an Jiaotong University, Xi’an, Shaanxi 710049, People’s Republic of China;2. National Key Laboratory of Schock Wave and Detonation Physics, Institute of Fluid Physics, CAEP, Mianyang 621900, People’s Republic of China |
| |
Abstract: | Pb0.94−xLa0.04Srx[(Zr0.6Sn0.4)0.84Ti0.16]O3 (x=0,0.02,0.04,0.06) antiferroelectric ceramics were fabricated via conventional solid-state reaction. The increase of Sr content enhanced the stability of antiferroelectric phase, which resulted in the rise of phase transition fields and energy density. When x=0.06, the releasable energy density was 1.52 J/cm3 and the efficiency was 93.3% under 129 kV/cm. The pulsed discharge current was also measured to evaluate the energy release properties. Under 129 kV/cm, the obtained current density could be as high as 165.5 A/cm2. The pulsed discharge energy density was 1.21 J/cm3 and 90% of that could be released in less than 200 ns. The high energy density, high efficiency and fast energy release time indicate that the obtained AFE ceramics are very promising for pulsed power capacitors. |
| |
Keywords: | Antiferroelectric Energy storage Pulsed power capacitor |
本文献已被 ScienceDirect 等数据库收录! |
|