| 环氧树脂固化度对粉末涂层性能的影响 |
| |
| 引用本文： | 崔志明,杨亚江. 环氧树脂固化度对粉末涂层性能的影响[J]. 塑料工业, 2001, 29(3): 37-39 |
| |
| 作者姓名： | 崔志明 杨亚江 |
| |
| 作者单位： | 1. 武汉化工学院科研产业处,
2. 华中科技大学化学系, |
| |
| 摘 要： | 研究了固化度对粉末涂层性能的影响。结果表明,环氧与聚酯配比可在一定范围内进行调整,消光固化剂B68用量为6：4份,固化度达80％以上时,涂层有较好的性能;对应的光泽度为4％;在100％固化度时,胶化时间最短,降低固化度,可延长胶化时间。
|
| 关 键 词： | 环氧树脂涂层 固化 粉末涂层 性能 消光固化剂 粉末涂料 |
| 修稿时间： | 2000-11-24 |
Effect of Solidification Degree of Epoxy Resin on Properties of Powder Coating |
| |
| CUI Zhiming,Yang Yajiang. Effect of Solidification Degree of Epoxy Resin on Properties of Powder Coating[J]. China Plastics Industry, 2001, 29(3): 37-39 |
| |
| Authors: | CUI Zhiming Yang Yajiang |
| |
| Abstract: | The effect of solidification degree on the properties of powder coating was studied.The results showed the compounding ratio of epoxy resin/polyester could be regulated,when the content of extinct curing agent B68 was 6.4 PHR and the solidification degree was higher than 80%,the coating properties were quite good,with a glossiness of 4%;when the solidification degree was 100%,the gelling time shortened,the decrease of the solidification degree could prolong the gelling time. |
| |
| Keywords: | Epoxy Resin Coating Curing Coating Property Extinct Curing Agent |