| Abstract: | Two kinds of 980MPa grade cold rolled dual phase steels have been developed by designing C-Si-Mn and C-Si-Mn-Nb alloy systems.The microstructure of martensite in Nb-free steel is consisted of lath martensite and twined martensite with the volume fraction of 67%.However,the main hard phase in Nb-containing one is twined martensit with the volume percent of 59%.The size of martensite islands in Nb-containing steel is from 1μm to 3μm,and the size of NbC precipitates is from 15nm to 40nm.As to Nb-containing steel,the yield strength,tensile strength,yield ratio and elongation are 501MPa,1035MPa,0.48 and 17.5% respectively.Futhermore,Nb-containing steel has higher working hardening rate value above the critical strain 6.5%.And it decreases slowly with increasing the strain.This is mainly because of ultrafine grain size and nano-precipitates in ferrite,which improves the compatibility of phases and reduces the stress concentration at the phase interface. |