Novel multiferroic La0.95Sb0.05FeO3 orthoferrite

A series of La_1−xSb_xFeO₃ was prepared using the conventional solid state method. XRD revealed the formation of the orthorhombic structure with space group Pbnm. The data showed that, the molar magnetic susceptibility and coercive field H_C were increased from 9.16 × 10⁻³ to 26.9 × 10⁻³ emu g⁻¹ mol and 1196 to 5465 Oe from for LaFeO₃ to La_0.95Sb_0.05FeO₃, respectively. The coercive field (H_C) of the sample with x = 0.05 increased 6 times than that of the parent LaFeO₃ and the saturation magnetization (M_s) was increased from 0.1614 emu g⁻¹ for the parent LaFeO₃ to 0.2654 emu g⁻¹ for the doped sample_. The dielectric constant (?′) was increased with increasing the Sb³⁺ content. The ac conductivity (σ) increases from 2.36 × 10⁻³ Ω⁻¹ m⁻¹ for the LaFeO₃ to 30 × 10⁻³ Ω⁻¹ m⁻¹ for the sample La_0.95Sb_0.05FeO₃ at T = 553 K and frequency 1 MHz. The sample La_0.95Sb_0.05FeO₃ is concluded to be a novel single phase multiferroic material.