Self-controlled growth of Fe3BO6 crystallites in shape of nanorods from iron-borate glass of small templates

Fe₃BO₆ can be an ideal compound for devising functional magnetic and dielectric properties in a single material for multiple applications such as electrodes, gas sensors, or medical tools. Useful to tailor such properties, here we report on a self-controlled Fe₃BO₆ growth in a specific shape of nanorods from a supercooled liquid precursor (an inorganic polymeric liquid or glass) of an initial composition (100 − x)B₂O₃ − xFe₂O₃, x = 40–50 mol%. B₂O₃ as a strong glass former co-bridges the Fe³⁺ ions in oxygen polygons primarily in a 2-D interconnected polymer network so that it dictates preferably a 1-D directional growth on the reaction Fe³⁺ species in form of a compound Fe₃BO₆, a favorable phase to nucleate and grow when annealing a precursor at 500–800 °C in ambient air. Distinct nanorods with a diameter ∼200 nm and 40–100 μm length have been formed on 10–15 min annealing a sample in microwave at moderate temperature 550 °C. A bonded surface B₂O₃ layer (15–25 nm thickness) has grown on the Fe₃BO₆ of the nanorods in situ in a specific structure. XPS bands in the Fe³⁺, B³⁺ and O²⁻ species confer this model structure. A local BO₃ → BO₄ conversion has incurred in the boroxol (B₃O_4.5)_n, n → ∞, rings in the surface layer, showing three distinct IR bands at 1035, 1215 and 1425 cm⁻¹.