Solubility Limit of La in the Lead Zirconate-Titanate System |
| |
Authors: | W. A. SCHULZE T. G. MILLER J. V. BIGGERS |
| |
Affiliation: | Materials Research Laboratory, The Pennsylvania State University, University Park, Pennsylvania 16802 |
| |
Abstract: | The disappearing-phase method was used to determine the extent of the solid-solution region of the PLZT system for conventionally sintered ceramics prepared at 1100° and 1300°C in a PbO atmosphere provided by pbZrO3. A decrease in the firing temperature from 1300° to 1100°C lowers the solubility limit by 5 to 8 at.% La. Beyond the limits of solubility, additional La forms La2Zr2O7 and/or La2Ti2O7. The limit determined by the disappearing-phase method (1300°C firing) is compared to values determined by the parametric method. The Curie temperature is stabilized at 5 at.% La for modified PbZrO3 (1300°C firing). |
| |