Hydrogen permeation during zinc-manganese alloy plating

Electrodeposition of metals from solution is usually accompanied by the simultaneous discharge of hydrogen ions or water molecules. When hydrogen is liberated at an iron/steel surface during electrodeposition, a portion of the hydrogen is absorbed by the metal surface and then diffuses into the interior. The diffused hydrogen produces some detrimental effects, such as reduction in ductility and loss in mechanical strength, leading to hydrogen embrittlement. The present paper reports investigations on hydrogen permeation measurements in zinc-manganese alloy deposition using a modified electrode clamp for easy removal and fixing of the electrode. Hydrogen permeation studies indicate that the porosity of the deposit increases in the following order:Zn-Mn(14.3%), Zn-Mn(2.4%), Zn-Mn(24.8%) and Zn-Mn(37.5%).This is in agreement with the corrosion data obtained which indicates that Zn-Mn alloy deposits with low manganese content show better performance than pure zinc deposits.