Effects of neodymium rich rare earth elements on microstructure and mechanical properties of as cast AZ31 magnesium alloy

Abstract

The effects of neodymium rich rare earth elements RE(Nd)] on microstructure and mechanical properties of as cast AZ31 magnesium alloy were investigated. The microstructures of as cast AZ31–xRE(Nd) alloys display a dendrite configuration, and the secondary dendrite spacing of the α-Mg phase was decreased with the increasing Nd content. The addition of RE(Nd) resulted in the formation of Al₂Nd and Mg₁₂Nd phases. Mechanical properties were improved significantly due to grain refinement and precipitation of intermetallic phases. When the amount of RE is 1·0 wt-%,The as cast AZ31 alloy reached its maximum tensile strength of 249 MPa at room temperature, yield strength of 169 MPa and elongation of 9·0%.