Abstract: | AbstractThe effects of neodymium rich rare earth elements [RE(Nd)] on microstructure and mechanical properties of as cast AZ31 magnesium alloy were investigated. The microstructures of as cast AZ31–xRE(Nd) alloys display a dendrite configuration, and the secondary dendrite spacing of the α-Mg phase was decreased with the increasing Nd content. The addition of RE(Nd) resulted in the formation of Al2Nd and Mg12Nd phases. Mechanical properties were improved significantly due to grain refinement and precipitation of intermetallic phases. When the amount of RE is 1·0 wt-%,The as cast AZ31 alloy reached its maximum tensile strength of 249 MPa at room temperature, yield strength of 169 MPa and elongation of 9·0%. |