| ZA27纺锭锭底失效原因分析 |
| |
| 引用本文： | 弓金霞,彭竹琴,刘英.ZA27纺锭锭底失效原因分析[J].铸造技术,2011,32(11). |
| |
| 作者姓名： | 弓金霞 彭竹琴 刘英 |
| |
| 作者单位： | 中原工学院,河南郑州,450007 |
| |
| 摘 要： | 研究铸造锌铝合金ZA27与锡青铜QSn6.5-0.1的摩擦磨损性能.发现在相同条件下ZA27合金的耐磨性好于锡青铜QSn6.5-0.1,但用ZA27合金制作的纺锭锭底却不如用QSn6.5-0.1制作的耐用,其原因是ZA27合金在凝固过程中产生的组织缩松,在润滑条件下进行磨损试验时,容易使润滑油及磨损中产生的粉末填入其中,从而影响了磨损实验的准确性.
|
| 关 键 词： | 纺锭锭底 ZA27合金 锡青铜QSn6.5-0.1 磨损试验 |
Failure Analysis on Textile Spindle Base of ZA-27 Alloy |
| |
| GONG Jin-xia,PENG Zhu-qiu,LIU Ying.Failure Analysis on Textile Spindle Base of ZA-27 Alloy[J].Foundry Technology,2011,32(11). |
| |
| Authors: | GONG Jin-xia PENG Zhu-qiu LIU Ying |
| |
| Affiliation: | GONG Jin-xia,PENG Zhu-qiu,LIU Ying (Zhongyuan University of Technology,Zhengzhou 450007,China) |
| |
| Abstract: | The friction-wearing performances of casting ZA27 alloy and tin bronze QSn6.5-0.1 were studied.The results show that ZA27 alloys has a superior wear resistance to that of QSn6.5-0.1 under the same condition,but the wear resistance of spindle base of ZA27 alloy is inferior to that of QSn6.5-0.1.Since the shrinkage porosity formed during solidifying of ZA27 alloy will be filled with oil and powder produced in wearing test,the accuracy of experimental results are influenced. |
| |
| Keywords: | Spindle base ZA27 alloys QSn6 5-0 1 tin bronze Wear experiment |
| 本文献已被 CNKI 万方数据 等数据库收录！ |
|