Experimental comparison of N(1s) X-ray photoelectron spectroscopy binding energies of hard and elastic amorphous carbon nitride films with reference organic compounds

In this work, hard and elastic amorphous carbon nitride (a-CN_x) films were deposited by DC magnetron sputtering on heated Si(001) substrates at 400 °C. Nanoindentation results confirmed that the films were highly compliant and had high elastic recovery. X-ray photoelectron spectroscopy (XPS) was used to investigate nitrogen bonding by directly comparing the N(1s) spectra of a-CN_x with the N(1s) peak positions of a variety of organic compounds that were characterized in the same XPS system. The N(1s) XPS spectra of hard and elastic a-CN_x is resolved into two dominant intensity contributions at 398.5 and 400.6 eV. We show that the N(1s) spectra of a-CN_x do not conclusively support a film-structure model with nitrogens bonded to sp³ carbons. We offer an alternate interpretation based on the presented data and previous XPS, nuclear magnetic resonance (NMR), and computational work. Together, the data suggest that hard and elastic a-CN_x consists of an sp² carbon network and that single-atom vacancy defects, as found in a graphite layer, may be present in the material. This implies that the low binding energy N(1s) component at 398.5 eV may be due to pyridine-like nitrogen bonded at the perimeter of a vacancy defect.