| 精铸模具钢热锻模的应用及寿命的提高 | |
| 引用本文： | 崔向红,姜启川,王树奇,李俊义. 精铸模具钢热锻模的应用及寿命的提高[J]. 吉林大学学报(工学版), 2005, 35(6): 567-0572 |
| 作者姓名： | 崔向红 姜启川 王树奇 李俊义 |
| 作者单位： | 1. 吉林大学,材料科学与工程学院,长春,130022 2. 江苏大学,材料科学与工程学院,江苏,镇江,212013 3. 长春丰东热处理有限公司,长春,130012 |
| 基金项目： | “863”国家高技术研究发展计划项目（2002AA331180）;国家计委产业化前期关键技术与成套设备研制开发项目（1999317）. |
| 摘 要： | 为了稳定和提高精铸热锻的使用寿命,研究了其失效形式和机理。研究结果表明:材质及工艺决定了精铸热锻模具呈现不同的失效形式和寿命。不恰当的材质及工艺导致热锻模具出现早期断裂失效,失效形式不合理,寿命较低。经改进材质及工艺后,热磨损、塑性变形为主要失效形式,而未出现早期断裂失效,寿命得到明显提高,稳定在6000~7000件,高于锻造模具钢80%以上。 |
| 关 键 词： | 材料失效及保护 热锻模具 精铸模具 失效分析 使用寿命 失效形式 |
| 文章编号： | 1671-5497（2005）06-0567-05 |
| 收稿时间： | 2005-04-28 |
| 修稿时间： | 2005-04-28 |
Application and Improvement of Service Life of Hot-forging Dies Prepared by Cast Steel |
|
| CUI Xiang-hong,JIANG Qi-chuan,WANG Shu-qi,LI Jun-yi. Application and Improvement of Service Life of Hot-forging Dies Prepared by Cast Steel[J]. Journal of Jilin University:Eng and Technol Ed, 2005, 35(6): 567-0572 | |
| Authors: | CUI Xiang-hong JIANG Qi-chuan WANG Shu-qi LI Jun-yi |
| Affiliation: | 1.College of Materials Science and Engineering,Jilin University, Changchun 130022 ,China; 2. College of Materials Science and Engineering,Jiangsu University, Zhenjiang 212013, China; 3. Changchun Fengdong Heat Treatment Company, Changchun 130012 ,China |
| Abstract: | To improve and stabilize the service life of hot-forging die fabricated by cast die steel,the failure modes and mechanism were analyzed.Results show that different failure modes and lives are dependent on the material composition and subsequent processing.Improper material composition and processing can cause earlier fracture failure and short life happened to the hot-forging dies.With improvement of material composition and processing,the failure modes demonstrate predominately elevated wear and plastic deformation,and no earlier failure occurred,leading to a considerable improvement of service life and a stable number of 6000~7000 times,80% more than forging steel dies. |
| Keywords: | material failure and protection hot-forging die cast-steel die failure analysis service life failure pattern |