Mixed mode I/II fracture of 2024-T3 friction stir welds

For the first time, a series of mixed mode I/II fracture experiments have been performed on both base material and three families of friction stir welds (FSWs) in 6.4 mm thick, 2024-T351 aluminum plate; the FSW joints are designated hot, medium and cold due to the level of nominal weld energy input per unit weld length (specific weld energy) during the joining process.Results from the fracture tests indicate that the measured critical crack opening displacement (COD) at a fixed distance behind the crack tip properly correlates both load-crack extension response and microstructural fracture surface features for both the base metal and all FSWs, providing measure of a quantitative fracture toughness. The COD values also indicate that transition from mode I to mode II dominant crack growth occurs at lower loading angles for FSW joints having higher specific weld energy input, with a truly mixed mode I/II COD measured during crack growth in the medium FSW joint. Using results from recent detailed FSW metallographic studies, specific features in the fracture process are correlated to the FSW microstructure. Finally, the observed ductile crack growth path in all three welds tends to exit the under-matched FSW weld region as the far-field applied shear loading is increased, with the medium FSW being the only case where the flaw remained within the FSW region for all combinations of shear and tensile loading.