NO decomposition and reduction by CH4 over Sr/La2O3

Both NO decomposition and NO reduction by CH₄ over 4%Sr/La₂O₃ in the absence and presence of O₂ were examined between 773 and 973 K, and N₂O decomposition was also studied. The presence of CH₄ greatly increased the conversion of NO to N₂ and this activity was further enhanced by co-fed O₂. For example, at 773 K and 15 Torr NO the specific activities of NO decomposition, reduction by CH₄ in the absence of O₂, and reduction with 1% O₂ in the feed were 8.3·10^?4, 4.6·10^?3, and 1.3·10^?2 μmol N₂/s m², respectively. This oxygen-enhanced activity for NO reduction is attributed to the formation of methyl (and/or methylene) species on the oxide surface. NO decomposition on this catalyst occurred with an activation energy of 28 kcal/mol and the reaction order at 923 K with respect to NO was 1.1. The rate of N₂ formation by decomposition was inhibited by O₂ in the feed even though the reaction order in NO remained the same. The rate of NO reduction by CH₄ continuously increased with temperature to 973 K with no bend-over in either the absence or the presence of O₂ with equal activation energies of 26 kcal/mol. The addition of O₂ increased the reaction order in CH₄ at 923 K from 0.19 to 0.87, while it decreased the reaction order in NO from 0.73 to 0.55. The reaction order in O₂ was 0.26 up to 0.5% O₂ during which time the CH₄ concentration was not decreased significantly. N₂O decomposition occurs rapidly on this catalyst with a specific activity of 1.6·10^?4 μmol N₂/s m² at 623 K and 1220 ppm N₂O and an activation energy of 24 kcal/mol. The addition of CH₄ inhibits this decomposition reaction. Finally, the use of either CO or H₂ as the reductant (no O₂) produced specific activities at 773 K that were almost 5 times greater than that with CH₄ and gave activation energies of 21–26 kcal/mol, thus demonstrating the potential of using CO/H₂ to reduce NO to N₂ over these REO catalysts.