Surface modification of LiNi0.5Mn1.5O4 by ZrP2O7 and ZrO2 for lithium-ion batteries

The spinel LiNi_0.5Mn_1.5O₄ has been surface modified separately with 1.0 wt.% ZrO₂ and ZrP₂O₇ for the purpose of improving its cycle performance as a cathode in a 5-V lithium-ion cell. Although the modifications did not change the crystallographic structure of the surface-modified samples, they exhibited better cyclability at elevated temperature (55 °C) compared with pristine LiNi_0.5Mn_1.5O₄. The material that was surface modified with ZrO₂ gave the best cycling performance, only 4% loss of capacity after 150 cycles at 55 °C. Electrochemical impedance spectroscopy demonstrated that the improved performance of the ZrO₂-surface-modified LiNi_0.5Mn_1.5O₄ is due to a small decrease in the charge transfer resistance, indicating limited surface reactivity during cycling. Differential scanning calorimetry showed that the ZrO₂-modified LiNi_0.5Mn_1.5O₄ exhibits lower heat generation and higher onset reaction temperature compared to the pristine material. The excellent cycling and safety performance of the ZrO₂-modified LiNi_0.5Mn_1.5O₄ electrode was found to be due to the protective effect of homogeneous ZrO₂ nano-particles that form on the LiNi_0.5Mn_1.5O₄, as shown by transmission electron microscopy.