The structural and electric properties of Li- and K-substituted Bi0.5Na0.5TiO3 ferroelectric ceramics

The structure, dielectric properties and phase transition of lithium and potassium modified Bi_0.5Na_0.5TiO₃ ceramics were investigated widely. The phase transition behavior with respect to changes in composition and temperature was investigated using X-ray diffraction analysis, dielectric and ferroelectric characterizations. The experimental results show that there is a diffusion phase transition in (Na_1−xK_x)_0.5Bi_0.5TiO₃ ceramics at T_m and the diffuseness of the phase transition is more obvious for the samples near the morphotropic phase boundary. In (Na_1−xLi_x)_0.5Bi_0.5TiO₃ system, due to the space charge polarization induced by ions conductivity, the low frequency permittivity increases so remarkably at high temperature that the peak of maximum permittivity vanishes. The hysteresis loops at different temperatures indicate that there is no existence of anti-ferroelectrics in lithium and potassium modified Bi_0.5Na_0.5TiO₃ ceramics above the depolarization temperature T_d. The depolarization reason is that the tetragonal nonpolar phase occurs and leads to the macro-micro domain transformation at about T_d.