Growth of lanthanum oxide films for application as a gate dielectric in CMOS technology

We have investigated properties of insulating lanthanum oxide (La₂O₃) films in connection with the replacement of silicon oxide (SiO₂) gate dielectrics in new generation of CMOS devices. The La₂O₃ layers were grown using metal organic chemical vapour deposition (MOCVD) at 500 °C. X-ray diffraction analysis revealed polycrystalline character of the films grown above 500 °C. The X-ray photoemission spectroscopy detected lanthanum carbonate as a principal impurity in the films and lanthanum silicate at the interface with silicon. Density of oxide charge, interface trap density, leakage currents and dielectric constant ( κ) were extracted from the C-V and I-V measurements. Electrical properties, in particular dielectric constant of the MOCVD grown La₂O₃ are discussed with regard to the film preparation conditions. The as grown film had κ11. Electrical measurements indicate possible presence of oxygen vacancies in oxide layer. The O₂-annealed La₂O₃ film had κ17.