| Abstract: | The degree of crystallinity of polyetheretherketone (PEEK) has been measured using both the density gradient technique (DGT) and differential scanning calorimetry (DSC). The difference in results between the methods was shown to depend on crystallization taking place during the heating scan in the DSC. By freezing the sample at different stages of the DSC thermogram and measuring its crystallinity in the density gradient column, the existence of induced crystallization for PEEK was established. Though this induced crystallization is not visible in the DSC thermogram, it must be taken into account when comparing the degree of crystallinity measured by the two methods. The induced crystallization was in turn interpreted as a result of an increase in crystal perfection that is also commonly observed during the initial stages of the annealing process. Accordingly, the effect of annealing on the crystallinity was also investigated. DSC scans on annealed samples exhibited a small endothermic peak at approximately 10°C above the annealing temperature. This peak was observed in both neat PEEK and its carbon fiber-reinforced composite. Annealed PEEK shows, therefore, two melting transitions, a low one which depends on the annealing temperature and a high one which is independent of annealing temperature conditions. Collectively, the results of this study demonstrate that processing conditions and morphological features must be considered in characterizing semicrystalline-based matrix polymers for high performance composites. |